Lexan LUX9616G (EXRL0945) is a UV stabilized high viscosity, flame retardant polycarbonate featuring non brominated and non chlorinated FR system with diffusion effect and thin wall FR performance providing good colorstability under heat exposure. Developed for LED applications. It meets WEEE/RoHS requirements for various applications.
防火阻燃，抗紫外线，为LED应用研发， 高粘度
Lexan LUX9616G物性表
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, yld, Type I, 50 mm/min
630
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min
660
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min
6
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
80
%
ASTM D 638
Tensile Modulus, 5 mm/min
23400
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
960
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
22000
kgf/cm2
ASTM D 790
Tensile Stress, yield, 50 mm/min
62
MPa
ISO 527
Tensile Stress, break, 50 mm/min
58
MPa
ISO 527
Tensile Strain, yield, 50 mm/min
6
%
ISO 527
Tensile Strain, break, 50 mm/min
75
%
ISO 527
Tensile Modulus, 1 mm/min
2230
MPa
ISO 527
Flexural Stress, brk, 12.5 mm/min
95
MPa
ISO 178
Flexural Modulus, 2 mm/min
2250
MPa
ISO 178
IMPACT
Value
Unit
Standard
Izod Impact, notched, 23°C
15
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
713
cm-kgf
ASTM D 3763
Izod Impact, notched 80*10*3 +23°C
15
kJ/m2
ISO 180/1A
THERMAL
Value
Unit
Standard
Vicat Softening Temp, Rate B/50
141
°C
ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed
125
°C
ASTM D 648
CTE, -40°C to 40°C, flow
6.8E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
6.7E-05
1/°C
ASTM E 831
Ball Pressure Test, 125°C +/- 2°C
PASSES
-
IEC 60695-10-2
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
123
°C
ISO 75/Af
Relative Temp Index, Elec
125
°C
UL 746B
Relative Temp Index, Mech w/impact
115
°C
UL 746B
Relative Temp Index, Mech w/o impact
125
°C
UL 746B
PHYSICAL
Value
Unit
Standard
Specific Gravity
1.2
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.6 - 0.8
%
SABIC Method
Melt Flow Rate, 300°C/1.2 kgf
7
g/10 min
ASTM D 1238
Density
1.2
g/cm3
ISO 1183
Water Absorption, (23°C/sat)
0.35
%
ISO 62
Moisture Absorption (23°C / 50% RH)
0.15
%
ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg
7
cm3/10 min
ISO 1133
ELECTRICAL
Value
Unit
Standard
Hot Wire Ignition {PLC)
3
PLC Code
UL 746A
High Ampere Arc Ign, surface {PLC}
1
PLC Code
UL 746A
Comparative Tracking Index (UL) {PLC}
3
PLC Code
UL 746A
FLAME CHARACTERISTICS
Value
Unit
Standard
UL Recognized, 94V-0 Flame Class Rating (3)
1.5
mm
UL 94
Glow Wire Flammability Index 960°C, passes at
1
mm
IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm
850
°C
IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.5 mm
850
°C
IEC 60695-2-13
Source GMD, last updated:2015/07/23
Processing
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 280 - 310 | °C |
| Nozzle Temperature | 270 - 290 | °C |
| Front - Zone 3 Temperature | 280 - 310 | °C |
| Middle - Zone 2 Temperature | 270 - 290 | °C |
| Rear - Zone 1 Temperature | 260 - 280 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 80 - 110 |
°C |
201-111
201-15
2014R-111
201R-111
2030
2034E
203R-111
221R BK1B408
221R GY2B422
221R-111
221R-701
221R-71004
223R
223R WH9521
223R-111
241-111
241-111N
241-LA888
241R
241R WH9B307
241R-111
241R-111(2)
241R-111L
241R-701
241R-WH4113
243R
243R-111
244R
244R-111
244R-701
2814R-131
2870-111
2870-21317
3010G
3020G
3030G
303-111
305
310