High Viscosity, UV-stabilized grade for ophthalmic lenses.
高粘度，抗紫外线，验光透镜
Sabic LEXAN OQ1022物性表
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, yld, Type I, 50 mm/min
630
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min
730
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min
6.3
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
125
%
ASTM D 638
Tensile Modulus, 50 mm/min
23100
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
940
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
24500
kgf/cm2
ASTM D 790
Tensile Stress, yield, 50 mm/min
61
MPa
ISO 527
Tensile Stress, break, 50 mm/min
71
MPa
ISO 527
Tensile Strain, yield, 50 mm/min
6
%
ISO 527
Tensile Strain, break, 50 mm/min
140
%
ISO 527
Tensile Modulus, 1 mm/min
2400
MPa
ISO 527
Flexural Stress, yield, 2 mm/min
94
MPa
ISO 178
Flexural Modulus, 2 mm/min
2200
MPa
ISO 178
IMPACT
Value
Unit
Standard
Izod Impact, notched, 23°C
93
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
1
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
866
cm-kgf
ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C
NB
kJ/m2
ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C
NB
kJ/m2
ISO 180/1U
Izod Impact, notched 80*10*3 +23°C
70
kJ/m2
ISO 180/1A
Izod Impact, notched 80*10*3 -30°C
12
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
75
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
15
kJ/m2
ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm
NB
kJ/m2
ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm
NB
kJ/m2
ISO 179/1eU
THERMAL
Value
Unit
Standard
Vicat Softening Temp, Rate B/50
150
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed
139
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
129
°C
ASTM D 648
CTE, -40°C to 40°C, flow
7.74E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
7.74E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, flow
7.6E-05
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow
7.89E-05
1/°C
ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C
P
-
IEC 60695-10-2
Vicat Softening Temp, Rate B/50
143
°C
ISO 306
Vicat Softening Temp, Rate B/120
144
°C
ISO 306
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
126
°C
ISO 75/Ae
PHYSICAL
Value
Unit
Standard
Specific Gravity
1.19
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.6 - 0.8
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm (5)
0.5 - 0.7
%
SABIC Method
Melt Flow Rate, 300°C/1.2 kgf
7.4
g/10 min
ASTM D 1238
Density
1.2
g/cm3
ISO 1183
Water Absorption, (23°C/sat)
0.32
%
ISO 62
Moisture Absorption (23°C / 50% RH)
0.15
%
ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg
6
cm3/10 min
ISO 1133
Source GMD, last updated:2004/09/14
Processing
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 48 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 310 - 330 | °C |
| Nozzle Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 310 - 330 | °C |
| Middle - Zone 2 Temperature | 300 - 320 | °C |
| Rear - Zone 1 Temperature | 290 - 310 | °C |
| Mold Temperature | 80 - 115 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
EXL1492C
EXL401-799
EXL4419-739
EXL9112 GY
EXL9134
EXL9134 BK
EXL9330 BK1A068
EXL9330 GY4B058
EXL9414T 7B1D086T
EXL943 GY
EXRL0086 NA9A048T
EXRL0109
EXRL0238
FLC95
FXD171R 8A8D016X
FXD171R WH1427X
FXD921A WH8C104X
GR1210
HF1110
HF1130
HF1130R
HP4-1H111
HPX4 1H8A005T
HPX8R NA8A005T
IR2240-111
LF1520A-111
LGK4010-731L
LS1-6164
LS2-414LT
ML4351R-80118
ML6411-76701
ML765-222(粉)
ML9330 BK1E519
OQ1022-111
OQ1030-111S