Highest impact extrusion ABS for sheet and blow molding applications. FDA food contact compliant.
食品级
CYCOLAC EX39F物性表
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, yld, Type I, 5 mm/min
35
MPa
ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min
28
MPa
ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min
3.5
%
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min
108
%
ASTM D 638
Tensile Modulus, 5 mm/min
1680
MPa
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
57
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
1900
MPa
ASTM D 790
IMPACT
Value
Unit
Standard
Izod Impact, notched, 23°C
464
J/m
ASTM D 256
Izod Impact, notched, -30°C
320
J/m
ASTM D 256
Instrumented Impact Total Energy, 23°C
39
J
ASTM D 3763
THERMAL
Value
Unit
Standard
Vicat Softening Temp, Rate B/50
106
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed
91
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
77
°C
ASTM D 648
CTE, -40°C to 40°C, flow
1.01E-04
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
1.17E-04
1/°C
ASTM E 831
Relative Temp Index, Elec
60
°C
UL 746B
Relative Temp Index, Mech w/impact
60
°C
UL 746B
Relative Temp Index, Mech w/o impact
60
°C
UL 746B
PHYSICAL
Value
Unit
Standard
Specific Gravity
1.03
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.7 - 0.9
%
SABIC Method
Melt Viscosity, 240°C, 100 sec-1
15200
poise
ASTM D 3825
Melt Volume Rate, MVR at 220°C/10.0 kg
4
cm3/10 min
ISO 1133
FLAME CHARACTERISTICS
Value
Unit
Standard
UL Recognized, 94HB Flame Class Rating (3)
1.52
mm
UL 94
Source GMD, last updated:2014/03/13
Processing
Parameter | ||
Sheet Extrusion | Value | Unit |
Drying Temperature | 90 - 95 | °C |
Drying Time | 2 - 4 | hrs |
Maximum Moisture Content | 0 | % |
Melt Temperature | 210 - 240 | °C |
Barrel - Zone 1 Temperature | 195 - 210 | °C |
Barrel - Zone 2 Temperature | 200 - 220 | °C |
Barrel - Zone 3 Temperature | 205 - 230 | °C |
Barrel - Zone 4 Temperature | 210 - 235 | °C |
Adapter Temperature | 200 - 225 | °C |
Die Temperature | 210 - 240 | °C |