High heat, low emissions ABS+PC blend.
| CYCOLAC DL100 is a high heat, high impact, low emissions ABS/PC blend. |
| 耐热高冲击强度 |
|
Property |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 5 mm/min | 44 | MPa | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 90 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 2240 | MPa | ASTM D 638 | |
| Hardness, Rockwell R | 104 | - | ASTM D 785 | |
| Tensile Stress, yield, 5 mm/min | 46 | MPa | ISO 527 | |
| Tensile Stress, yield, 50 mm/min | 45 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3.5 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 60 | % | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 3.4 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 10 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2200 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 69 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2250 | MPa | ISO 178 | |
| Hardness, H358/30 | 91 | MPa | ISO 2039-1 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 700 | J/m | ASTM D 256 | |
| Izod Impact, notched, 23°C, 6.4mm | 550 | J/m | ASTM D 256 | |
| Izod Impact, notched 80*10*4 +23°C | 35 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 34 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 14 | kJ/m2 | ISO 179/1eA | |
| THERMAL | Value | Unit | Standard | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 105 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 88 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 90 | °C | ASTM D 648 | |
| CTE, 23°C to 60°C, flow | 9.8E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 9.8E-05 | 1/°C | ISO 11359-2 | |
| Vicat Softening Temp, Rate B/50 | 105 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 107 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 104 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 87 | °C | ISO 75/Ae | |
| Relative Temp Index, Elec | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Mold Shrinkage on Tensile Bar, flow (2) (5) | 0.5 - 0.7 | % | SABIC Method | |
| Density | 1.08 | g/cm3 | ISO 1183 | |
| Melt Flow Rate, 220°C/10.0 kg | 7 | g/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 8 | cm3/10 min | ISO 1133 | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94HB Flame Class Rating (3) | 1.5 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value (3) | 3 | mm | UL 94 | |
| Source GMD, last updated:2014/06/13 |
|
Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 - 100 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.1 | % |
| Melt Temperature | 250 - 280 | °C |
| Nozzle Temperature | 245 - 275 | °C |
| Front - Zone 3 Temperature | 250 - 280 | °C |
| Middle - Zone 2 Temperature | 250 - 280 | °C |
| Rear - Zone 1 Temperature | 230 - 260 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 40 - 80 | °C |