High impact ABS for sheet extrusion and blow molding applications.
高抗冲击ABS 挤出吹塑
CYCOLAC EX58物性表
|
Property |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 5 mm/min | 39 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 30 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3.1 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 31.6 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 2080 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 66 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2160 | MPa | ASTM D 790 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 432 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 299 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 37 | J | ASTM D 3763 | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 106 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 93 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 80 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 1.01E-04 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.04E-04 | 1/°C | ASTM E 831 | |
| Relative Temp Index, Elec | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.03 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.6 - 0.8 | % | SABIC Method | |
| Melt Viscosity, 240°C, 100 sec-1 | 14000 | poise | ASTM D 3825 | |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 4 | cm3/10 min | ISO 1133 | |
| ELECTRICAL | Value | Unit | Standard | |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 4 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 4 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94HB Flame Class Rating (3) | 1.52 | mm | UL 94 | |
| Source GMD, last updated:2014/03/13 |
|
Processing |
| ? Recommend initial lower temperatures settings to avoid material degradation/hang-up in die. |
| Parameter | ||
| Sheet Extrusion | Value | Unit |
| Drying Temperature | 80 - 95 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 215 - 260 | °C |
| Barrel - Zone 1 Temperature | 170 - 200 | °C |
| Barrel - Zone 2 Temperature | 180 - 220 | °C |
| Barrel - Zone 3 Temperature | 190 - 225 | °C |
| Barrel - Zone 4 Temperature | 200 - 240 | °C |
| Adapter Temperature | 205 - 250 | °C |
| Die Temperature | 205 - 250 | °C |
| Roll Stack Temp - Top | 90 - 95 | °C |
| Roll Stack Temp - Middle | 95 - 105 | °C |
| Roll Stack Temp - Bottom | 100 - 105 | °C |